Reinforced Composite Hard Felt - Sheet
Packaging Details: Standard export carton or customized
Delivery time: 30 days
Payment Terms: Western Union
Supply Ability: 100,000kg per month
Operating temperature in air: < 350 ℃
Working temperature in vacuum: < 2200 ℃
Operating temperature in atmosphere: < 3000 ℃
Carbon content: above 98%
Density: 0.18-0.32g.cm3
Material thickness: 5-300mm
Plate length: 10--3000mm
Plate width: 10-2000mm
Plate thickness: 5-300mm
Physical and chemical indicators:
| main material |
PAN-CF / asphalt-CF / viscose-CF |
Sheet specifications |
length(mm) |
10-3000 |
| Bulk density(g/CM3)) |
0.25-0.30 |
width(mm) |
10-2000 |
| Thermal conductivity |
0.15-0.25(25℃)0.40-0.45(1400℃)
|
thickness(mm) |
5-300 |
|
Barrel specifications
|
diameter(Φ) |
Φ100-Φ2500 |
| Carbon content(％) |
≧98 |
Wall thickness(T) |
5-150 |
| bending strength(Gpa) |
1.8-3.5 |
Tube height |
100-3000 |
| Flexural strength(Gpa) |
1.5-2.8 |
Use environment
|
air(℃) |
≦350 |
| ash content(ppm) |
≦300 |
vacuum(℃) |
≦2200 |
| Processing temperature |
First ≧1800
Second ≧2200
|
Inert atmosphere(℃) |
≦3000 |
Temperature resistance: 2200 ℃ in vacuum, 3000 ℃ in inert gas
Reinforced Composite Hard Felt: small heat capacity, low thermal conductivity, good thermal insulation performance, rapid heating and rapid cooling without deformation
The density of this product is 0.18-0.32g/cm3. The surface can be coated with graphite paper or carbon cloth, carbon cloth and graphite paper, graphite paper can be sandwiched between each felt. It can prevent surface fluff, gas leakage (convection), and protect its surface (prevent loss) and increase the strength of hard felt.
It has the advantages of high rigidity, self-supporting, high strength, no short fiber loss, and low thermal conductivity that traditional insulation materials do not have.
Reinforced Composite Hard Felt Application:
1. Aerospace industry: hot isostatic pressing furnace, heat treatment, sintering, brazing, hot pressing furnace
2. Semiconductor industry: drawing silicon single crystal furnace, vacuum metallurgy
3. Metal heat treatment: heat treatment furnace, sintering furnace, brazing furnace
4. Carbon fiber production: induction heating or resistance heating carbonization furnace, graphitization furnace
5. The production of composite materials: pyrolytic carbon and pyrolytic graphite, chemical vapor deposition, or other composite materials
6. Energy materials: vanadium or other redox battery materials
Hunan MTR New Material Technology Co., Ltd. has perfect production technology and equipment, we can customize products of various sizes and shapes to meet your needs for various vacuum and high temperature furnace insulation materials. Sincerely welcome your inquiries.
Product Tags:
|
|